ʻO kahi hoʻoheheʻe ʻana i ka lapalapa ahi no SK Polyester ES500 (UL94 V0 helu).

ʻO kahi hoʻoheheʻe ʻana i ka lapalapa ahi no SK Polyester ES500 (UL94 V0 helu).

I. Hoʻolālā Hoʻolālā Hoʻolālā

1. Hoʻolikelike substrate
   • SK Polyester ES500: He polyester thermoplastic me kahi mahana hana maʻamau o 220–260°C. Pono ka pale ahi e kū i kēia pae wela.
   • Nā Koina Koʻikoʻi: ʻO ka pale ʻana i ka lapalapa ahi (V0), nā waiwai mechanical (ikaika tensile/impact), a me ka hoʻoili ʻana i ka wai.
2. Synergistic Flame Retardant System
   • ʻO Ultrafine Aluminum Hydroxide (ATH): ʻO ka hoʻopaʻa ahi mua, ka wai maloʻo endothermic. Pono ka hoʻouka ʻana e hoʻohālikelike i ka pale ahi a me nā waiwai mechanical.
   • Aluminum Hypophosphite: Char-forming synergist, hana pū me ATH e hana i kahi hopena phosphorus-aluminum synergistic, hoʻomaikaʻi i ka maikaʻi char.
   • Zinc Borate: Char enhancer, hoʻopaʻa i ka uahi, a hana i kahi pale paʻa me ATH.
   • ʻO MCA (Melamine Cyanurate): ʻO ke kinoea-phase flame retardant, hoʻoheheʻe i ka oxygen a pale i ka hoʻoheheʻe ʻana.

II. Manaʻo ʻia ka hoʻokumu ʻana (ka pākēneka kaumaha)

III. Nā Mana Kaʻina Hana Nui

1. Hoʻohalahala ʻana
   • Mamua o ka lapaʻau ʻana: E hoʻoinu i ka ATH a me ka alumini hypophosphite i 1% KH-550 ethanol solution no 2 hola, a laila maloʻo ma 80°C.
   • Kaʻina huikau:
     1. Base resin + dispersant + hui hoʻohui → Haʻahaʻa-wikiwiki hui ʻana (500 rpm, 5 min).
     2. Hoʻohui i ka ATH/aluminum hypophosphite i hoʻololi ʻia → ʻO ka shear kiʻekiʻe (2500 rpm, 20 min).
     3. Hoʻohui i ka zinc borate/MCA/PTFE → Ka hui ʻana o ka wikiwiki haʻahaʻa (800 rpm, 10 min).
   • Mea lako: Twin-screw extruder (nā ʻāpana wela: kahi hānai 200 ° C, wahi hoʻoheheʻe 230 ° C, make 220 ° C).
2. Hoʻoponopono i ka mana wela
   • E hōʻoia i ka wela hoʻoheheʻe <250°C no ka pale ʻana i ka MCA decompose (MCA decomposes ma 250–300°C).
   • ʻO nā pellets ʻoluʻolu wai ma hope o ka extrusion e pale i ka neʻe ʻana o ka lapalapa ahi.

IV. Mechanism Synergistic Hoʻopaʻa ʻia i ke ahi

1. ATH + Aluminum Hypophosphite
   • Hoʻopau ʻo ATH i ka wela a hoʻokuʻu i ka mahu wai, e hoʻoheheʻe i nā kinoea hiki ke hoʻā.
   • Hoʻopili ka alumini hypophosphite i ka hoʻokumu ʻana o ka char dense (AlPO₄), e ālai ana i ka hoʻoili wela.
2. Zinc Borate + MCA
   • Hana ʻo Zinc borate i pale aniani ma luna o nā māwae char.
   • Hoʻoheheʻe ʻia ʻo MCA e hoʻokuʻu i ka NH₃, hoʻoheheʻe i ka oxygen a pale i nā hopena radical manuahi.
3. PTFE Anti-Dripping
   • Hoʻokumu ʻia ka micropowder PTFE i kahi pūnaewele fibrous, e hōʻemi ana i ka hopena o ka hoʻoheheʻe ʻana.

V. Hoʻoponopono a me nā pilikia

VI. Nā Ana Hōʻoia

1. Hoʻāʻo UL94 V0:
   • 1.6 mm a me 3.2 mm specimens, huina manawa kuni < 50 sec ma hope o elua puhi ana, aole kulu ignition.
2. LOI: Manaʻo ≥30% (ʻoiaʻiʻo ≥28%).
3. Nā Pono Mechanical:
   • Ka ikaika tensile > 40 MPa, ka ikaika hopena > 5 kJ/m² (ASTM standard).
4. ʻO ke kūpaʻa wela (TGA):
   • ʻO ke koena Char ma 800°C > 20%, ka wela o ka decomposition mua > 300°C.

VII. Hoʻohālike Hoʻohālike

Hoʻokō pono kēia hoʻolālā a me ka hoʻolālā kaʻina hana i ka UL94 V0 flame retardancy no SK Polyester ES500 ʻoiai ke kaupaona nei i ka hana a me nā waiwai mechanical. Manaʻo ʻia nā hoʻāʻo liʻiliʻi e hōʻoia i ka hoʻopuehu ʻana ma mua o ka hoʻoponopono pono ʻana (e laʻa, ke kaupaona ʻana i ka alumini hypophosphite a me MCA). No ka hoʻonui hou ʻana i ke ahi, e noʻonoʻo e hoʻohui i 2% boron nitride nanosheets (BNNS) ma ke ʻano he mea hoʻopihapiha hoʻopihapiha wela.

More info., pls contact lucy@taifeng-fr.com