ʻO ka PVC Flame Retardant Masterbatch Reference Formulation
ʻO ka hoʻolālā a me ka hoʻolālā ʻana o ka PVC flame retardant masterbatch formulations, e hoʻopili ana i nā mea pale ahi e kū nei a me nā ʻāpana synergistic koʻikoʻi, e kuhikuhi ana i ka UL94 V0 flame retardancy (hiki ke hoʻololi ʻia i ka V2 ma ka hōʻemi ʻana i nā mea hoʻohui).
I. Manaʻo Kumu Kumu (PVC ʻoʻoleʻa)
ʻO ka hoʻokumu ʻana i ke ahi e pale ai i ke ahi:
| ʻāpana | Ke hoʻouka nei (wt%) | wehewehe hana |
|---|---|---|
| PVC resin (ʻano SG-5) | 40-50% | Mea matrix, ʻoi aku ka haʻahaʻa o ka ʻaila-absorption grade |
| Aluminum hypophosphite | 12-15% | ʻO ke kumu ʻakika no ka hoʻokumu ʻana i ka pehu, hoʻopau i ka ʻulaʻula |
| Zinc borate | 8-10% | ʻO ka hoʻopau ʻana i ka uahi synergistic, pane me ka HCl mai PVC decomposition |
| Aluminum hydroxide i hoʻololi ʻia i ka ʻili | 10-12% | ʻO ka hoʻoluʻu endothermic, pono i ka hoʻopili ʻana i ka silane coupling agent coating (decomposition temp. match PVC processing) |
| Antimony trioxide (Sb₂O₃) | 3-5% | Core synergist, hoʻonui i ka pale ahi ma o Cl-Sb synergy |
| Zinc molybdate (hoʻopau i ka uahi) | 5-8% | Hoʻohui ʻia, hoʻemi i ka nui o ka uahi (ki no ka hoʻokō DIN 4102) |
| Dipentaerythritol (DPE) | 2-3% | ʻO ke kōkua hoʻoheheʻe ʻana, hoʻomaikaʻi i ka mana hoʻoheheʻe |
| Mea hoʻopaʻa wela (Ca-Zn composite) | 3-4% | Pono e pale i ka hoʻohaʻahaʻa wela i ka wā e hana ai |
| Plasticizer (DOP a i ʻole eco-alternative) | 0-8% | Hoʻoponopono no ka paʻakikī (koho no ka PVC paʻa) |
| Lubricant (calcium stearate) | 1-1.5% | Hoʻomaikaʻi i ka hana, pale i ka pili ʻana o ka roller |
| Kokua hana (ACR) | 1-2% | Hoʻonui i ka plastification a me ka hoʻopuehu masterbatch |
II. Nā Kuʻuna Hoʻoponopono Kiʻi
- Pūnaehana Synergy Hoʻopaʻa ʻAla
- Cl-Sb Synergy: ʻO ka chlorine inherent o PVC (56%) i hui pū ʻia me 3-5% Sb₂O₃ hana i kahi pale SbCl₃, e hiki ai ke hoʻopaneʻe i ka lapalapa ahi.
- Hoʻopau i ka uahi: ʻO Zinc molybdate + zinc borate e hoʻemi ana i ka nui o ka uahi ma> 40% (ASTM E662).
- Hoʻonui Char: Aluminum hypophosphite + DPE hoʻopuka i ka char phosphoric ester char i hoʻopaʻa ʻia ma 200–250°C, e uku ana i ka hemahema o ka char mua o PVC.
- Hiki ke hoʻololi
- Pākuʻi Mahana: Aluminum hypophosphite (decomposition ≥250 ° C) a me Al (OH) ₃ i hoʻololi ʻia i ka ʻili (paʻa i> 200 ° C) kūpono i ka hana PVC (160-190 ° C).
- Hōʻoia Paʻa: ʻO nā stabilizers Ca-Zn e pale i ka hoʻohaʻahaʻa resin mai ka hoʻokuʻu ʻana o HCl; Kōkua ʻo ACR i ka plastification i nā ʻōnaehana hoʻopiha piha.
- Kaulike hana
- Ka nui o ka hoʻouka ʻana o ka lapalapa ahi: 35–45%, paʻa ikaika tensile ≥80% (maʻamau ≥40 MPa no PVC paʻa).
- No ka maʻalahi (PVC maʻalahi), e hoʻololi i ka DOP me 8% epoxidized soybean aila (ʻelua plasticizer/flame retardant).
III. Nā ana hoʻāʻo a me ka hōʻoia
Hoʻopaʻa ahi:
- UL94 V0 (1.6 mm mānoanoa)
- Hoʻopaʻa ʻia ʻo Oxygen Index (LOI) ≥32%
Kāohi uahi:
- ʻO ka hoʻāʻo ʻana o ke keʻena uahi NBS: ʻO ka nui o ka ʻike kikoʻī kikoʻīDs≤150 (ke ʻano lapalapa)
Nā Pono Mechanical:
- ʻO ka ikaika tensile ≥35 MPa (ʻoʻoleʻa), elongation ma ka haʻihaʻi ≥200% (maʻalahi)
Paʻa wela:
- Hōʻoia ʻo DMA ʻaʻohe hāʻule modulus ma 180°C.
IV. Kumukuai & Hooponopono Pilikino
ʻAno ʻano kumu kūʻai haʻahaʻa:
- E ho'ēmi i ka zinc molybdate i 3%, e hoʻololi hapa Al(OH)₃ me Mg(OH)₂ (hoʻonui i ka 15%).
ʻO ka hoʻonā Antimony-Free:
- Wehe iā Sb₂O₃, hoʻohana i ka 2% aluminika diethylphosphinate + 5% nano-kaolin (haʻahaʻa haʻahaʻa; pono 3 mm mānoanoa no V0).
ʻO ka mea nui o ka uahi:
- Hoʻohui i ka 1% silicone resin-coated carbon black e hoʻemi hou i ka nui o ka uahi ma 15%.
V. Nā alakaʻi alakaʻi
- Kaʻina huikau:
Pvc resin → stabilizer + lubricant → flame retardants (haʻahaʻa a kiʻekiʻe kiʻekiʻe) → plasticizer (spray-added hope). - Hoʻoponopono Mahana:
Nā ʻāpana extruder twin-screw: 160°C (feeding) → 170°C (melting) → 180°C (mixing) → 175°C (make head). - Kumu
Manaʻo 50% hoʻouka; e hoʻoheheʻe i ka 1: 1 me ka PVC puʻupaʻa no ka hoʻohana hope ʻana i ka hoʻoheheʻe ʻana.
Hoʻohālikelike kēia ʻano hoʻohālikelike i ka hiki ʻana o ka lapalapa ahi kiʻekiʻe, ka uahi haʻahaʻa, a me ka paʻa o ka hana. Aʻo ʻia nā hoʻokolohua liʻiliʻi ma mua o ka hoʻonui ʻana, me nā hoʻoponopono e pili ana i ke ʻano huahana (pepa, kelepona, etc.).